上海斯米克焊材

Category
类 别
 Trade-
Mark
牌 号
 Equivalent to China Standard
相当*
 Characteristics & application
特性和用途
 Equivalent to AWS
相当AWS
 
Hard-surfacing
硬
面

堆

焊
 D 667 
 EDZCr-B-15 
 HRc≥48. Resistance to wear, gas corrosion and oxidation. Hardfacing of blast furnace hopper and cracker part.
HRc≥48，*、耐气蚀、抗氧化。堆焊高炉料钟、破碎机件

   
D 802 
 EDCoCr-A-03 
 HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter.
HRc38-47，耐热、耐蚀、*。堆焊高温工件如热剪切刀刃
 ECoCr-A 
 
D 812 
 EDCoCr-B-03 
 HRc45-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve.
HRc45-50，耐热、耐蚀、*。堆焊高温工件如内燃机阀
 ECoCr-B 
 
D 822 

    HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler.
HRc≥53，耐热、*，但抗冲击性差。堆焊锅炉旋转叶轮

   
D 832 
 EDCoCr-C-03 
 HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way.
HRc≥50，耐热、*。堆焊高温工件如热轧导轨
 ECoCr-C 
 
D 842 
 EDCoCr-D-03 
 HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die.
HRc28-38，耐蚀、抗热疲劳，具有加工硬化性。堆焊热锻模

   
　
Cast iron

铸

铁 
 Z 308 
 EZNi 
 Pure nickel, excellent general properties. Used to weld thin cast iron part and repair welding machined surface, such as guided way of machine tool.
纯镍，综合性能好。铸铁薄件及加工面补焊用，如机床导卫
 ENi-Cl 
 
Z 408 
 EZNiFe 
 Iron nickel, high strength and excellent ductility. Repair welding of important gray cast iron and nodular cast iron, such as cylinder cap.
镍铁，强度高、塑性好。重要灰铸铁及球铁焊补用，如汽缸盖
 ENiFe-Cl 
 
Z 508 
 EZNiCu-1 
 Copper nickel, good machinability and bad crack resistance. Repair welding of sand hole and gray cast iron machined surface subject to no load.
镍铜，易加工，但抗裂性较差。不受力的灰铸铁加工面及砂眼补焊
 ENiCu-B 
 
　
Copper alloys

铜

合

金 
 Cu 107 
 ECu 
 Red copper, atmosphere and sea water corrosion and excellent electric conductivity. Welding of red copper such as electrical copper row.
紫铜，耐大气，海水腐蚀，导电性好。紫铜焊接用，如导电铜排
 ECu 
 
Cu 207 
 ECuSi 
 Silicon bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass.
硅青铜，耐蚀、强度高。铜、硅青铜及黄铜焊接用
 ECuSi 
 
Cu 227 
 ECuSnB 
 Tin phosphor bronze, corrosion resistance and high strength. Welding of copper, silicon bronze and brass.
锡磷青铜，耐蚀、强度高。铜、硅青铜及黄铜焊接用
 ECuSn-C 
 
Cu 237 
 ECuAl 
 Aluminum bronze, wear and corrosion and high strength. Welding or surfacing of copper alloys.
铝青铜，*、耐蚀，强度高。铜合金焊接或堆焊用
 ECuAl-A2 
 
Aluminum alloys

铝
合
金 
 Al 109 
 TAl 
 Pure aluminum, excellent corrosion resistance and middle strength. Welding of pure aluminum.
纯铝，耐蚀性好，但强度不高，纯铝焊接用
 E1100 
 
Al 209 
 TAlSi 
 Silicon aluminum, good crack resistance and wide range of usage. Welding of aluminum alloys other than aluminum magnesium alloys.
铝硅，抗裂性好，通用性大。铝合金焊接用，不宜焊接铝镁合金
 E4043 
 
Al 309 
 TAMn 
 Manganese aluminum, corrosion resistance and high strength. Welding of aluminum alloys.
铝锰，强度高，耐蚀。铝合金焊接用
 E3003 
 
Nickel alloys
镍合金 
 Ni 102 
 ENi-1 
 Pure nickel. Welding and surfacing of nickel and nickel to steel.
纯镍，用于镍、镍与钢的焊接与堆焊
 ENi-1 
 
Ni 207 
 ENiCu-7 
 Copper nickel. Welding and surfacing of copper nickel and copper nickel to steel.
镍铜，用于镍铜、镍铜与钢的焊接与堆焊
 ENiCu-7 
 


    焊丝

Category
类 别 
 Trade
mark
牌 号 
 Chemical composition
主要成份(%) 
 Characteristics & application
特性和用途 
 Equivalent to AWS
相当AWS 
 
Hardfacing

硬

面

堆

焊 
 S 101 
 C3 Cr28 Ni4
Si3.5 Fe Rem.
 HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，*、耐气蚀、抗氧化。堆焊铲斗齿，泵套

   
S 111 
 C1 Cr29 W5
Co Rem.
 HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高温下*、耐蚀。堆焊高温高压阀门
 ECoCr-A 
 
S 112 
 C1.5 Cr29 W8
Co Rem.
 HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高温下*、耐蚀。堆焊阀门，热轧孔型
 ECoCr-B 
 
S 113 
 C2.5 Cr30 W17
Co Rem.
 HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高温下*、耐热，但抗冲击性差。堆焊螺旋送料机用

   
S 114 
 C2.5 Cr30 W12
Co Rem.
 HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高温下*、耐热，但抗冲击较差。堆焊牙轮钻头
 ECoCr-C 
 
Copper
alloys

 
铜

　
合

　
金 
 S 201 
 Sn1 Si0.3Mn0.3
Cu Rem.
 Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
机械性能好，抗裂性好。紫铜气焊及氩弧焊用
 ERCu 
 
S 211 
 Si3 Mn1
Cu Rem.
 Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
机械性能好，铜合金氩弧焊及钢的MIG钎焊用
 ERCuSi-Al 
 
S 212 
 Sn5 Cu Rem. 
 Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
*性好。铜合金氩弧焊及钢的堆焊用
 ERCuSn-A 
 
S 213 
 Sn8 Cu Rem. 
 Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
*性好。铜合金氩弧焊及钢的堆焊用
 ERCuSn-C 
 
S 214 
 Al7.5 Cu Rem. 
 Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
*、耐蚀。铜合金氩弧焊及钢的堆焊用
 ERCuAl-A1 
 
S 215 
 Al9 Cu Rem. 
 Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
*、耐蚀。铜合金氩弧焊及钢的堆焊用
 ERCuAl-A2 
 
S 221 
 Cu60 Sn1 Si0.3
Zn Rem.
 Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

   
S 221F 
 Cu60 Sn1 Si 0.3
Zn Rem.
 S221 welding rod coated with flux.
外涂焊剂的S221焊丝

   
S 222 
 Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.
 Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
 RBCuZn-C 
 
S 222F 
 Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.
 S222 welding rod coated with flux.
外涂焊剂的S222焊丝
 RBCuZn-C 
 
S 223 
 Cu59 Sn0.6
Zn Rem.
 Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔点约900℃。铜、钢、铸铁钎焊用
 RBCuZn-A 
 
S 224 
 Cu62 Si0.5
Zn Rem.
 Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁

   
Copper
alloys
铜

合

金 
 S 225 
 Cu48 Ni10
Zn Rem.
 Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔点约935℃。高强度,钎焊钢、镍及硬质合金用
 RBCuZn-D 
 
S 225F 
 Cu48 Ni10
Zn Rem.
 S225 welding rod coated with flux.
外涂焊剂的S225焊丝
 RBCuZn-D 
 
S 226 
 Cu60 Sn0.3
Si0.2 Zn Rem.
 Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁

   
S 227 
 Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.
 Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁
 RBCuZn-B 
 
S 229 
 Cu55 Ni6 Mn4
Zn余
 Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔点约920℃。高强度,钎焊钢、镍及硬质合金用

   
Aluminum alloys

铝

合

金 
 S 301 
 Al≥99.5 
 Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蚀。纯铝气焊、氩弧焊用
 ER1100 
 
S 311 
 Si5 Al Rem. 
 Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金
 ER4043 
 
S 321 
 Mn1.3 Al Rem. 
 Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用

   
S 331 
 Mg5 Mn0.4
Al Rem.
 Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蚀，强度高。铝合金氩弧焊用
 ER5183 
 <
   

钎焊料

Category
类 别 
 Trade-mark
牌号 
 Specification
规 格 
 Melting
Point
熔点(℃) 
 Chemical
composition
主要成份(%) 
 Application
用 途
 Equivalent
to AWS
相当AWS 
 
Copper
zinc
铜锌 
 L103 
 Wire & rod
丝 
 885-888 
 Cu54 Zn Rem. 
 Brazing of copper, bronze and steel, subjected to low load.
钎焊铜、青铜和钢等受力不大工件 

   
L104 
 Foil
箔 
 890-930 
 Cu57 Mn2
Co2 Zn Rem. 
 Brazing of carbide cutting tool.
钎焊硬质合金刀具

   
Copper
phosphorus

　
铜磷 
 L201 
 Cast rod, wire & rod, powder
铸条、丝、粉 
 710-800 
 P7 Cu Rem. 
 Brazing of copper and copper alloys.
钎焊铜及铜合金
 BCuP-2 
 
L204 
 Cast rod, wire
铸条、丝 
 640-815 
 P5 Ag15
Cu Rem. 
 Brazing of copper, copper alloys, silver and molybdenum etc.
钎焊铜及铜合金、银、钼等金属。 
 BCuP-5 
 
L205 
 Cast rod, wire & rod, powder
铸条、丝、箔 
 640-800 
 P6 Ag5
Cu Rem. 
 Brazing of copper and copper alloys.
钎焊铜及铜合金
 BCuP-3 
 
L207 
 Cast rod, wire & rod
铸条、丝 
 640-770 
 P7 Ag5
Cu Rem. 
 Brazing of copper and copper alloys.
钎焊铜及铜合金
 BCuP-7 
 
L209 
 Cast rod, wire
铸条、丝 
 684-710 
 P7 Ag2
Cu Rem. 
 Brazing of copper and copper alloys.
钎焊铜及铜合金。 
 BCuP-6 
 
　Silver
base

银基 
 L302 
 Wire & rod
丝 
 745-775 
 Ag25 Cu40
Zn Rem. 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等

   
L303 
 Wire & rod
丝 
 660-725 
 Ag45 Cu30
Zn余 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等
 BAg-5 
 
L303F 
 Flux coated rod
涂药丝 
 660-725 
 Ag45 Cu30
Zn Rem. 
 L303 coated with flux, the same application as L303.
外涂钎剂的L303，用途与L303相同 
 BAg-5 
 
L304 
 Foil
箔 
 690-775 
 Ag50 Cu34
Zn Rem. 
 Brazing of copper, copper alloys and steel etc.
钎焊铜及铜合金、钢等
 BAg-6 
 
L308 
 Wire & rod
丝 
 779-780 
 Ag72 Cu Rem. 
 Brazing of copper and nickel under vacuum or reducing protective atmosphere.
铜和镍的真空或还原保护气氛钎焊 
 BAg-8 
 
L312 
 Wire & rod
丝 
 595-605 
 Ag40.Cu.Zn.Cd 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等 

   
L313 
 Wire & rod
丝 
 625-635 
 Ag50.Cu.Zn.Cd 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等
 BAg-1a 
 
L321 
 Wire & rod
丝 
 615-650 
 Ag56.Cu.Zn.Sn 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等
 BAg-7 
 
L323 
 Wire & rod
丝 
 665-755 
 Ag30.Cu.Zn.Sn 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等

   
L325 
 Wire & rod
丝 
 645-685 
 Ag45.Cu.Zn.Sn 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等 
 BAg-36 
 
L326 
 Wire & rod
丝 
 650-720 
 Ag38.Cu.Zn.Sn 
 Brazing of copper, copper alloys, steel and stainless steel etc.
钎焊铜及铜合金、钢及不锈钢等
 BAg-34 
 
Aluminum base
铝基 
 L400 
 Cast rod, wire & rod
铸条、丝 
 577-582 
 Si11.5
Al Rem. 
 Brazing of aluminum and aluminum alloys.
铝及铝合金的钎焊 
 BAlSi-4 
 
L401 
 Cast rod
铸条 
 525-535 
 Si5 Cu28
Al Rem. 
 Brazing of aluminum and aluminum alloys.
铝及铝合金的钎焊 

   
Tin lead
锡铅 
 L600 
 Wire & rod
丝 
 183-185 
 Sn60 Sb≤0.8
Pb Rem. 
 Soldering of fusible metals and heat-treated part.
易熔金属及热处理件的钎焊
 60Sn 
 
L601 
 Wire & rod
丝 
 183-227 
 Sn18 Sb2
Pb Rem. 
 Soldering of copper, copper alloys and galvanized iron plain sheet.
铜及铜合金、镀锌铁皮的钎焊。 
 18Sn 
 
L602 
 Wire & rod
丝 
 183-256 
 Sn30 Sb2
Pb Rem. 
 Soldering of copper, brass, copper alloys and galvanized iron plain sheet.
铜、黄铜、铁、镀锌铁皮的钎焊
 30Sn 
 
L603 
 Wire & rod
丝 
 183-235 
 Sn40 Sb2
Pb Rem. 
 Soldering of copper, copper alloys, steel and zinc parts.
铜及铜合金、钢、锌制零件的钎焊
 40Sn 
 
L604 
 Wire & rod
丝 
 183-222 
 Sn90 Sb≤0.15
Pb Rem. 
 Soldering of copper and steel for food and medicine field.
食品、医疗所需铜、钢等金属的钎焊
 90Sn 
 
L605 
 Wire & rod
丝 
 232-240 
 Ag5 Sn95 
 Soldering of copper and steel for electrical and food field.
电器、食品所需铜、钢等金属的钎焊

   
L608 
 Wire & rod
丝 
 295-305 
 Sn5.5 Ag2.5
Pb Rem. 
 Soldering of copper, copper alloys, steel and stainless steel.
铜及铜合金、钢及不锈钢的钎焊

   
Nickel base
镍基 
 L702 
 Powder
粉 
 970-1000 
 Cr7 B3 Si4
Ni Rem. 
 Brazing of stainless steel under vacuum or protective atmosphere.
不锈钢真空或保护气氛钎焊
 BNi-2 
 

气焊及钎焊熔剂

Category
类 别
 Trade-mark
牌 号
 Product name
名 称
 Characteristics & application
特性和用途
 
Gas
welding
气焊
 CJ301 
 Copper gas welding flux
铜气焊熔剂
 Melting point is about 650℃, flux for gas welding and brazing of copper and copper alloys.
熔点约650℃，铜及铜合金气焊或钎焊的助熔剂
 
CJ401 
 Aluminum gas welding flux
铝气焊熔剂
 Melting point is about 560℃, flux for gas welding of aluminum and aluminum alloys.
熔点约560℃，铝及铝合金气焊的助熔剂
 
Silver
brazing
银钎焊
 QJ101 
 Silver brazing flux
银钎焊熔剂
 Brazing flux of copper, copper alloys, steel and stainless steel within 550-750℃.
在550-750℃范围钎焊铜及铜合金、钢及不锈钢的助熔剂
 
QJ102 
 Silver brazing flux
银钎焊熔剂
 Brazing flux of copper, copper alloys, steel and stainless steel within 600-850℃.
在600-850℃范围钎焊铜及铜合金、钢及不锈钢的助熔剂
 
QJ102A 
 Silver brazing flux
银钎焊熔剂
 Brazing flux of copper, copper alloys, steel and stainless steel within 600-850℃. Non agglomeration.
在600-850℃范围钎焊铜及铜合金、钢及不锈钢。不易结块
 
QJ112 
 Silver brazing paste flux
膏状银钎焊熔剂 
 Brazing flux of copper, copper alloys, steel and stainless steel within 600-850℃.
在600-850℃范围钎焊铜及铜合金、钢及不锈钢的助熔剂
 
QJ103 
 Silver brazing flux
银钎焊熔剂
 Brazing flux of copper, copper alloys, steel and stainless steel within 550-750℃.
在550-750℃范围钎焊铜及铜合金、钢及不锈钢的助熔剂
 
Aluminum brazing
铝钎焊
 QJ201 
 Aluminum brazing flux
铝钎焊熔剂
 Brazing flux of aluminum and aluminum alloys within 450-620℃.
在450-620℃范围钎焊铝及铝合金的助熔剂
 
QJ207 
 Aluminum brazing flux
铝钎焊熔剂
 Brazing flux of aluminum and aluminum alloys within 560-620℃.
在560-620℃范围钎焊铝及铝合金的助熔剂
 

 
 